1. Characteristics: low density, high hardness
2. Purpose: Production of men's and women's sandals, leather shoes, and high-heeled soles
3. Characteristics of original solution
Product name | Exterior | Viscosity | density(g/cm3) | Storage stability £¨20 OCthe following£© | Package |
SX-P-8559 | Milky white liquid or waxy | 1300¡«1600 | 1.16¡«1.18 | 6 months | 18Kg/bucket |
SX-I-9722D | Transparent liquid without foreign matter | 200¡«400 | 1.18¡«1.20 | 3 months | 20Kg/bucket |
4. Catalysts and auxiliaries
The adding amount of SX-C-003 is 280¡À10g/18Kg, the adding amount of water is 60~130g/18Kg, and the adding amount of hardener SX-E-001 is 500-1500 g/18Kg.
5. Molding conditions and physical property values
Reactivity | Technical Parameters | project | physical value | experiment method |
Reference scale P+C/I | 100/93~95 | Sole molding density (g/cm3) | 0.35~0.45 | GB/T6638¡ª86 |
Operating temperature(oC) | 40~45/38~42 | hardness (A type) (C type) | 68~82 80~90 | GB/T3903¡ª4 |
milky white time(s) | 6~9 | Tensile Strength (MPa) | 4.5~5.5 | GB/T6344 |
rise time (s) | 35~49 | Elongation (%) | 300~420 | GB/T6344 |
free bubble density (g/cm3) | 0.16~0.20 | Tear strength (kn/m) | 20.0~25.0 | GB/T10808 |
Metal mold temperature (oC) | 50~60 | Embrittlement temperature
| -22~-27 | GB/T15256 |
Demold time (min) | 4.0~6.0 | Folding endurance test £¨Second-rate£¬23 oC£© |
| GB/T3903.1 |
|
| NBS wear resistance (%) (data after pre-skin removal) | ¡Ý20 | JCSS |
¡¤Long-term storage of P-8559 will cause the internal components to stratify, so stir evenly after heating and dissolving before use.
¡¤The density of free foam will vary depending on the season (temperature, humidity).
¡¤The demoulding time will increase as the thickness of the molded product increases.
¡¤The physical property data is obtained by testing a 6mm thick test piece.
¡¤Folding resistance conditions: The bending angle is 90 degrees, the frequency is 230 times/min, and an average of 2 6mm incisions are pre-cut at the bending area.
¡¤The above data is for reference only, and the specific data is subject to actual operation. If you need other physical property indicators, please contact our company.