1. Characteristics: low hardness, good elasticity
2. Purpose: production of travel shoe midsoles, casual shoe midsoles, and elastic handicrafts
3. Characteristics of original solution
?
Product name | Exterior | Viscosity | density(g/cm3) | Storage stability £¨20 OCÒÔÏ£© | Package |
SX-P-5013-1 | liquid or waxy | 13000¡«1600 | 1.16¡«1.19 | 6¸öÔÂ | 18Kg/bucket |
SX-I-9560 | Transparent liquid without foreign matter | 600¡«900 | 1.18¡«1.20 | 3¸öÔÂ | 20Kg/bucket |
4. Catalysts and auxiliaries
The adding amount of SX-C-003 is 260¡À5g/18Kg, the adding amount of water is 25-40g/18Kg, and the adding amount of hardener SX-E-001 is 0-500 g/18Kg.
5. Molding conditions and physical property values
NBS wear resistance (%) (data after pre-skin removal)
Reactivity | Technical Parameters | project | physical value | experiment method |
Reference scale P+C/I | 100/50~55 | Sole molding density(g/cm3) | 0.30~0.45 | GB/T6638¡ª86 |
Operating temperature (oC) | 39~43/38~42 | hardness (A type) (C type) | 25~45 35~54 | GB/T3903¡ª4 |
milky white time(s) | 6~9 | Tensile Strength (MPa) | 5.0~6.0 | GB/T6344 |
rise time (s) | 25~35 | Elongation (%) | 150~250 | GB/T6344 |
free bubble density (g/cm3) | 0.15~0.25 | Tear strength (kn/m) | 8~10 | GB/T10808 |
Metal mold temperature(oC) | 45~55 | Embrittlement temperature
| -25~-30 | GB/T15256 |
Demold time (min) | 5.0~7.0 | Folding endurance test £¨´Î£¬23 oC£© |
| GB/T3903.1 |
|
|
|
| JCSS |
¡¤Long-term storage of P-5013-1 will cause the internal components to stratify, so stir evenly after heating and dissolving before use.
¡¤The density of free foam will vary depending on the season (temperature, humidity).
¡¤The demoulding time will increase as the thickness of the molded product increases.
¡¤The physical property data is obtained by testing a 6mm thick test piece.
¡¤Folding endurance conditions: The bending angle is 90 degrees, the frequency is 230 times/min, and an average of two 6mm incisions are pre-cut at the bending area.
¡¤The above data is for reference only, and the specific data is subject to actual operation. If you need other physical property indicators, please contact our company.