1. Characteristics: low hardness, good fluidity, polyether type
2. Purpose: Production of insoles and linings, soft mid-low and soft armrest cushions and other handicrafts
3. Characteristics of original solution
Product name | Exterior | Viscosity | density(g/cm3) | Storage stability £¨20 OCÒÔÏ£© | Package |
SX-P-3530 | liquid or waxy | 600¡«800 | 1.16¡«1.19 | 6¸öÔÂ | 18Kg/bucket |
SX-I-3522 | Transparent liquid without foreign matter | 200¡«300 | 1.18¡«1.20 | 3¸öÔÂ | 20Kg/bucket |
4. Catalysts and auxiliaries
The adding amount of SX-C-001 is 260¡À5g/18Kg, the adding amount of water is 25-40g/18Kg, and the adding amount of hardener SX-E-001 is 0-500 g/18Kg.
5. Molding conditions and physical property values
Reactivity | Technical Parameters | project | physical value | experiment method |
Reference scale P+C/I | 100/42~45 | Sole molding density (g/cm3) | 0.30~0.70 | GB/T6638¡ª86 |
Operating temperature(oC) | 35~38/38~42 | hardness (A type) (C type) | 10~25 20~45 | GB/T3903¡ª4 |
milky white time(s) | 6~9 | Tensile Strength (MPa) | 5.0~6.0 | GB/T6344 |
rise time (s) | 25~35 | Elongation (%) | 350~450 | GB/T6344 |
free bubble density (g/cm3) | 0.15~0.25 | Tear strength(kn/m) | 10~13 | GB/T10808 |
Metal mold temperature (oC) | 45~55 | Embrittlement temperature
| -25~-30 | GB/T15256 |
Demold time (min) | 5.0~7.0 | Folding endurance test £¨Second-rate£¬23 oC£© |
| GB/T3903.1 |
|
| NBSWear-resistant£¨%£© £¨Data after pre-epidermal removal£© |
| JCSS |
¡¤The mixing ratio is based on the optimal mixing ratio value, which will vary with the type and amount of pigment additives added.
¡¤Long-term storage of P-3530 will cause the internal components to stratify, so stir evenly after heating and dissolving before use.¡¤The density of free foam will vary depending on the season (temperature, humidity).
¡¤The demoulding time will increase as the thickness of the molded product increases.
¡¤The physical property data is obtained by testing a 6mm thick test piece.
¡¤Folding endurance conditions: The bending angle is 90 degrees, the frequency is 230 times/min, and an average of two 6mm incisions are pre-cut at the bending area.
¡¤The above data is for reference only, and the specific data is subject to actual operation. If you need other physical property indicators, please contact our company.